Analysis of Densification Process and Structure of PM Al-Mg-Si-Cu-Fe and Al-Zn-Mg-Cu-Sn Alloys release_lzrsbd4a65bd5oas246laibiiu

by R. Bidulský, J. Bidulská, M. Actis Grande

Published in Archives of Metallurgy and Materials by Walter de Gruyter GmbH.

2014   Volume 59, p17-23

Abstract

<jats:title>Abstract</jats:title> The paper is focused on the role of the pressing pressure on the densification behaviour of PM aluminium alloys. Commercially aluminium based powders Al-Mg-Si-Cu-Fe and Al-Zn-Mg-Cu-Sn were used as materials to be investigated. The apparent density of the powder mixes was determined according to MPIF St. 04. A set of cylinder test specimen 55x10x10 mm<jats:sup>3 </jats:sup>was uniaxially pressed in a floating hardened steel die. Compaction pressures ranged from 50 MPa up to 700 MPa. Considering the densification of metal powders in uniaxial compaction, quantification of aluminium compaction behaviour was performed. The compressibility behaviour was evaluated, considering the effect on specimens, as well as on their microstructure. The development of compressibility values with pressing pressure enables to characterize the effect of particles geometry and matrix plasticity on the compaction process.
In application/xml+jats format

Archived Files and Locations

application/pdf  1.1 MB
file_djt6wuviw5bp3a2vztkk7lvhvq
www.degruyter.com (web)
web.archive.org (webarchive)
application/pdf  1.1 MB
file_zj4imuk5znej3jec5xsuzfzbye
yadda.icm.edu.pl (web)
web.archive.org (webarchive)
application/pdf  1.1 MB
file_rmaiw7db5nhrhb2tnzou773nvi
web.archive.org (webarchive)
content.sciendo.com (web)
Read Archived PDF
Preserved and Accessible
Type  article-journal
Stage   published
Date   2014-03-01
Container Metadata
Open Access Publication
In DOAJ
In ISSN ROAD
In Keepers Registry
ISSN-L:  1733-3490
Work Entity
access all versions, variants, and formats of this works (eg, pre-prints)
Catalog Record
Revision: 38a55046-fbbe-4e5f-b3f4-64a348e26feb
API URL: JSON