Effect of Tannic Acid Application on Durability of Bond of Etch and Rinse Adhesive Resins release_lizn5hskyvc7jfhxu4i6wkeakq

by Alireza Boruziniat, Mostafa Babazadeh, Mahshid Gifani, Monavar Nasirzadeh

Published in Journal of Dental Materials and Techniques by Mashhad University of Medical Sciences.

2017   p125-130

Abstract

Aim: To determine the effect of different concentrations and application times of tannic acid on bond strength to dentin. Materials and Methods: Occlusal surfaces of 180 human molars were randomly divided into two groups of immediate shear bond strength evaluation and evaluation after 2 months of storage in collagenase solution. Each group was divided into 10 subgroups according to the solutions applied: no additional treatment (control), chlorhexidine 2% (Positive control), tannic acid 20% (30s, 1 min, 3min, 5min) and Tannic acid 30% (30s, 1 min, 3 min, 5 min). Failure mode were assessed using a stereo-microscope. The data were statistically analyzed by One-way ANONA and Tukey's post hoc test. Results: There was no significant difference in immediate bond strength among experimental groups. However, after 2 months storage in collagenase solution, a significant difference was found among the groups.  Bond strengths of CHX and 20% TA applied for 3 minute were significantly higher than the control group. Conclusion: Use of tannic acid and chlorhexidine has no negative effect on immediate shear bond strength. However, their application significantly prevents compromised bond strength caused by storage in collagenase solution.
In text/plain format

Archived Files and Locations

application/pdf  335.2 kB
file_bvy3wtqhgrgn3hr42l462sdlvm
jdmt.mums.ac.ir (publisher)
web.archive.org (webarchive)
Read Archived PDF
Preserved and Accessible
Type  article-journal
Stage   published
Year   2017
Language   en ?
Journal Metadata
Open Access Publication
In DOAJ
Not in Keepers Registry
ISSN-L:  2252-0317
Work Entity
access all versions, variants, and formats of this works (eg, pre-prints)
Catalog Record
Revision: 02a1a930-3ec5-4376-9d02-dd34c3dc2770
API URL: JSON