@article{kováčik_emmer_2014,
title={Sintering of HDH Ti Powder},
volume={22},
DOI={10.2478/stu-2014-0009},
abstractNote={Abstract
Titanium powders prepared by hydro-dehydration process (HDH powder) were pressure less sintered in vacuum oven at different temperatures, time and green density. The sintering properties of powders of two particle sizes - 30 and 150 microns were investigated. The usual powder metallurgical (PM) results were observed, i.e., decreasing final porosity with increasing sintering temperature and time at constant heating rate. Higher green density leading to higher final density for both powder sizes was also observed. The obtained results will be used as comparative material for future sintering experiments of Ti based composites.},
publisher={Walter de Gruyter GmbH},
author={Kováčik and Emmer},
year={2014},
month={Dec}
}